Loctite® Fixmaster® 235641 EA 3471 2-Part Steel Putty, 25 lb Pail, Paste Form, Gray/White, Part A: 2.6/Part B: 1.5

99912-LOC MFG #: 235641
$1,768.15 / EA
Non-Stock Item
Loctite® Fixmaster® 235641 EA 3471 2-Part Steel Putty, 25 lb Pail, Paste Form, Gray/White, Part A: 2.6/Part B: 1.5
  • Applicable Materials: Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum
  • Application Time: 30 min
  • Base Type: Epoxy
  • Color: Gray/White
  • Container Size: 25 lb
  • Container Type: Pail
  • Country of Origin: US
  • Coverage: 278 sq-cm at 6 mm THK/0.45 kg
  • Curing Time: 6 hr
  • Flash Point: >93 deg C
  • Form: Paste
  • Manufacturer Name: Henkel
  • Mixing Ratio: 2.5:1 By Volume/6.25:1 By Weight
  • Odor/Scent: Part A: Slight/Musty, Part B: Ammoniacal
  • Request For Quote: No
  • Series: EA 3471
  • Shear Strength: 1395 psi
  • Specific Gravity: Part A: 2.6/Part B: 1.5
  • Temperature Rating: -30 to 105 deg C
  • Tensile Strength: 4900 psi
  • Type: 2-Part
  • VOC Content: <10 g/L
Loctite® Fixmaster® Steel Putty, 2-Part, Series: EA 3471, Pail Container, 25 lb Container, Epoxy Base, Composition: Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine, Paste Form, 278 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application Time, 6 hr Curing, Gray/White, Part A: Slight/Musty, Part B: Ammoniacal Odor/Scent, -30 to 105 deg C, Part A: 2.6/Part B: 1.5 Specific Gravity, >93 deg C Flash Point, 2.5:1 By Volume/6.25:1 By Weight Mixing Ratio, <10 g/L VOC, Applicable Materials: Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum, 4900 psi Tensile Strength, 1395 psi Shear Strength
QTY
Add to List
  • Standards
  • Application
  • Item Features
ABS Approved|CFIA Approved|ISO Certified|NAVSEA|NEHC|OSHA 29 CFR 1910.1200|GHS Certified
Filling Mild Steel and Forming Molds
  • Steel putty is a non-slumping, two-part, steel-filled putty
  • Will not sag or shrink
  • Rebuilds worn parts fast limits downtime
  • High steel content cures to a metal-like finish
  • Superior adhesion bonds well to all metal substrates
  • D 85 shore hardness
  • 35 to 40 gel time at 21 deg C
  • Epoxy resin part A, epoxy hardener part B