3M™ 2104A Electrical Insulating Resin, 3.46 oz Size A/2-Part Pouch, Green, Liquid Form, Specific Gravity: Part A: 1.04/Part B: 1
7100003209
MFG #: 2104A
$72.77
/ EA
Estimated Delivery 7 to 10 Business Days
- Manufacturer: 3M
- Series: 2104
- Container Type: Size A/2-Part Pouch
- Container Size: 3.46
- Form: Liquid
- Composition: Part A: 35 to 50% Phthalic Acid, Di-C11-14-Branched Alkyl, Esters, C13-Rich, 15 to 35% Polymethylene Polyphenylene Isocyanate, Part B: 55 to 75% Polypropylene Glycol Glycerol Triether, 5 to 20% n, n-Di 2-HydroxypropylAniLine
- Curing Time: 1 hr at 70 deg F/20 hr at 20 deg F
- Color: Green
- Odor/Scent: Isocyanate
- Temperature Rating: 0 to 130
- Specific Gravity: Part A: 1.04/Part B: 1
- Flash Point: 230 deg F Part A, >= 230 deg F Part B
- Brand: 3M™
3M™ Electrical Insulating Resin, Series: 2104, Size A/2-Part Pouch Container, 3.46 oz Container, Liquid Form, Composition: Part A: 35 to 50% Phthalic Acid, Di-C11-14-Branched Alkyl, Esters, C13-Rich, 15 to 35% Polymethylene Polyphenylene Isocyanate, Part B: 55 to 75% Polypropylene Glycol Glycerol Triether, 5 to 20% n, n-Di 2-HydroxypropylAniLine, 1 hr at 70 deg F, 20 hr at 20 deg F Curing, Green, Isocyanate Odor/Scent, 0 to 130 deg C, Part A: 1.04/Part B: 1 Specific Gravity, 230 deg F Part A, >=230 deg F Part B Flash Point
- Polyurethane material
- Container bag size A
- Gel time 18 min at 73 deg f
- Class B temperature range
- 70 shore a hardness
- 1000 vac or less voltage rating
- Part a -35 to 50% phthalic acid, Di-C11-14-branched alkyl, esters, C13-Rich, 15 to 35% polyethylene
- 98% elongation
- Has 18 min gel time at 73 deg f (23 deg C)
- Useful for replacing or repairing the jacket on both single- and multi-core power cables
- 444 psi tensile strength
- 72-N, 85 series used in these kits
- 0.28 % moisture absorption, 1:1 mixing ratio, pale yellow part A, black part B
- 524 V/mil dielectric strength
- Bonds to all modern cable jackets, bonds to itself
- Available in two part closed mixing pouch for easy mixing and pouring
- Tough, semi-flexible, excellent multi-purpose moisture sealing resin
- Room temperature cure, low viscosity
- Part a -35 to 50% phthalic acid, Di-C11-14-branched alkyl, esters, C13-Rich, 15 to 35% polyethylene
- 2 years shelf life
Polyurethane material
Container bag size A
Gel time 18 min at 73 deg f
Class B temperature range
70 shore a hardness
1000 vac or less voltage rating
Part a -35 to 50% phthalic acid, Di-C11-14-branched alkyl, esters, C13-Rich, 15 to 35% polyethylene polyphenylene isocyanate, 15 to 25 % 1,3-butadiene, homopolymer, hydroxyterminated, 5 -20 P,P-methylenebis(phenyl isocyanate), 0 to 10% 1,1-methylenebis(is
98% elongation
Has 18 min gel time at 73 deg f (23 deg C)
Useful for replacing or repairing the jacket on both single- and multi-core power cables
444 psi tensile strength
72-N, 85 series used in these kits
0.28 % moisture absorption, 1:1 mixing ratio, pale yellow part A, black part B
524 V/mil dielectric strength
Bonds to all modern cable jackets, bonds to itself
Available in two part closed mixing pouch for easy mixing and pouring
Tough, semi-flexible, excellent multi-purpose moisture sealing resin
Room temperature cure, low viscosity
Part a -35 to 50% phthalic acid, Di-C11-14-branched alkyl, esters, C13-Rich, 15 to 35% polyethylene polyphenylene isocyanate, 15 to 25 % 1,3-butadiene, homopolymer, hydroxyterminated, 5 -20 P,P-methylenebis(phenyl isocyanate), 0 to 10% 1,1-methylenebis(isocyanatobenzene), 0 to 0.5% phenyl isocyanate, part B-55 to 75% polypropylene glycol glycerol triether, 5 to 20% N,N-Di(2-hydroxypropyl) aniline, 5 to 20% phthalic acid, Di-C11-14-branched alkyl esters, C13-rich, 1 to 10 dipropylene glycol
2 years shelf life