Loctite® Fixmaster® 235641 EA 3471 2-Part Steel Putty, 25 lb Pail, Paste Form, Gray/White, Part A: 2.6/Part B: 1.5
99912-LOC
MFG #: 235641
$1,768.15
/ EA
Non-Stock Item
- Applicable Materials: Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum
- Application Time: 30 min
- Base Type: Epoxy
- Color: Gray/White
- Container Size: 25 lb
- Container Type: Pail
- Country of Origin: US
- Coverage: 278 sq-cm at 6 mm THK/0.45 kg
- Curing Time: 6 hr
- Flash Point: >93 deg C
- Form: Paste
- Manufacturer Name: Henkel
- Mixing Ratio: 2.5:1 By Volume/6.25:1 By Weight
- Odor/Scent: Part A: Slight/Musty, Part B: Ammoniacal
- Request For Quote: No
- Series: EA 3471
- Shear Strength: 1395 psi
- Specific Gravity: Part A: 2.6/Part B: 1.5
- Temperature Rating: -30 to 105 deg C
- Tensile Strength: 4900 psi
- Type: 2-Part
- VOC Content: <10 g/L
Loctite® Fixmaster® Steel Putty, 2-Part, Series: EA 3471, Pail Container, 25 lb Container, Epoxy Base, Composition: Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenediphenol, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine, Paste Form, 278 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application Time, 6 hr Curing, Gray/White, Part A: Slight/Musty, Part B: Ammoniacal Odor/Scent, -30 to 105 deg C, Part A: 2.6/Part B: 1.5 Specific Gravity, >93 deg C Flash Point, 2.5:1 By Volume/6.25:1 By Weight Mixing Ratio, <10 g/L VOC, Applicable Materials: Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel, Aluminum, 4900 psi Tensile Strength, 1395 psi Shear Strength
- Item Features
- Application
- Standards
- Steel putty is a non-slumping, two-part, steel-filled putty
- Will not sag or shrink
- Rebuilds worn parts fast limits downtime
- High steel content cures to a metal-like finish
- Superior adhesion bonds well to all metal substrates
- D 85 shore hardness
- 35 to 40 gel time at 21 deg C
- Epoxy resin part A, epoxy hardener part B
Filling Mild Steel and Forming Molds